ASTM D Standard Test Method for Air Permeability of Textile Fabrics. What This Test is Used For: This test method covers the measurement of the air. ASTM D – Tensile, Compressive and Flexural Creep and . ASTM D testing covers the measurement of the air permeability of textile fabrics. This test. This standard is issued under the fixed designation D ; the number interest. 1 This test method is under the jurisdiction of ASTM Committee D13 on Textiles.
|Published (Last):||3 October 2013|
|PDF File Size:||10.43 Mb|
|ePub File Size:||19.81 Mb|
|Price:||Free* [*Free Regsitration Required]|
It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Yarn crimp and weave influence the shape and area of the interstices between yarns wstm may permit yarns to extend easily.
In filtration, for example, efficiency is directly related to air permeability.
ASTM D – 18 Standard Test Method for Air Permeability of Textile Fabrics
The fabrics may be untreated, heavily sized, coated, resin-treated, or otherwise treated. The values stated in inch-pound units may be approximate. Link to Active This link will always route to the current Active version of the standard. As a minimum, ensure the test samples to be used asmt as homogeneous as possible, are drawn from the material from which the disparate test results were obtained, and are randomly assigned in equal number to each laboratory for testing.
If bias is found, either its cause must be found and corrected, or future test results for that material must be adjusted in consideration of the known bias. The test results from the two laboratories should be compared using a statistical test for unpaired data, at a probability level chosen prior to the testing series.
Air permeability also can be used to provide an indication of the breathability of weather-resistant and rainproof fabrics, or of coated fabrics in general, and to detect changes during the manufacturing process.
Fabrics with different surface textures on either side can have a different air permeability depending upon the direction of asm flow. Such yarn extension would open up the fabric, increase the free area, and increase the air permeability. Hot calendaring can be used to flatten fabric components, thus reducing air permeability.
Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of asmt standard. As twist increases, the circularity and density of the yarn increases, thus reducing the yarn diameter and the cover factor and increasing the air permeability. For example, a worsted gabardine fabric may have lower air permeability than a xstm hopsacking fabric. Historical Version s – view previous versions of standard.